B23r085 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B23R085 B:Baosteel, R: Series of magnetic domains oriented silicon steel sheet.23 : Thickness 0.23mm, 23/100 for the product thickness, in mm., 085/100 indicates that the product core loss not greater than 0.85w / kg.

B23P085 electromagnetic performance standards

NOTE:. A detector according to GB / T 3655-2008 (G-series and P-series), GB / T3789-2008 (R Series)
b . G-series and P-series samples were rolling direction, and incubated for 2 hours at 800 ℃ magnetically eliminate stress after annealing treatment can be tested
c . P17/50 represents the maximum magnetic flux density of 1.7T, a frequency of 50Hz, the unit kg sample of core loss.
d . B50 represents the magnetic field intensity corresponding to the intensity of the magnetic induction 5000A / m when.

B23R085 steel Features:
1 . stable performance: advanced equipment, manufacturing technology and strict management to ensure the stability of the magnetic and mechanical properties.
2 . excellent processing performance: high dimensional accuracy and a smooth surface for easy cutting and punching, slitting steel for high-speed blanking.
3 . excellent coating properties:. BS series of electrical steel insulation coating has excellent insulating properties, adhesion, punching, heat resistance and weldability, with anti-corrosion (oil and chemicals) role.
4 . high dimensional accuracy: Baosteel advanced equipment and manufacturing technology to ensure the BS series has excellent flatness, smooth surface, uniform thickness, with a small difference plate, lamination factor.

B23R085 steel application :

B23R085 steel mainly used in automotive, excavators, bulldozers, Various types of cranes etc.