B23P085 mainly low-carbon steel, requires a good cold bending and welding properties, as well as some of the press performance.

B23P090 mainly low-carbon steel, requires a good cold bending and welding properties, as well as some of the press performance.

B23P095 mainly low-carbon steel, requires a good cold bending and welding properties, as well as some of the press performance.

B23r080 is a soft magnetic alloy ferrosilicon very low carbon content, usually silicon content of 0.5 to 4.5%. Added silicon can improve iron resistivity and maximum permeability and lower coercive force, core loss (iron loss) and magnetic aging.

B23R085 B:Baosteel, R: Series of magnetic domains oriented silicon steel sheet.23 : Thickness 0.23mm, 23/100 for the product thickness, in mm., 085/100 indicates that the product core loss not greater than 0.85w / kg.

B23R090 B:Baosteel, R: Series of magnetic domains oriented silicon steel sheet.23 : Thickness 0.23mm, 23/100 for the product thickness, in mm., 090/100 indicates that the product core loss not greater than 0.90w / kg.