BR1500HS

BR1500HS steel Chemical Composition

Grade

C

Si

Mn

P

B

BR1500HS

0.20~0.25

≤0.40

1.0~1.5

≤0.015

≤0.0035

Remark : Cr,Ti,Nb can be added on a demand

BR1500HS steel sheet Mechanical Properties

Grade

Thickness
(mm)

Yield strength
(MPa)

Tensile strength
(MPa)

Elongation
A50
(%)

BR1500HS

1.75~4.0

≥320

≤800

≥13

1500 grade (Heat-treated)

950~1250

150~1800

≥6

Remark : The properties after hot stamping has a close relationship with process. Here only for reference.

Hot stamping is the process by deforming the heated steel in a mould to make parts, which take the advantage of a specific feature of metals that the ductility of metals increases and the yield strength decreases rapidly under a high temperature. The steel sheet is heated to the austenite temperature for hot stamping, and then rapidly cooled in the mould. By such a process, parts with tensile strength above 1400MPa can be manufactured.

BR1500HS steel plate/sheet preparation before welding : The mess on the welding area should be cleared to keep it clean and dry .

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As BR1500HS Mechanical and BR1500HS suppliers, we can supply BR1500HS Chemical, BR1500HS Mechanical and BR1500HS standard for you ,please contact us ：info@sg295steel.com