BW450

BW450 B : Baosteel,W:Wear Resistant Steel, 450:Brinell hardness value

BW450 steel are produced from processes of hot rolling, cutting into length and heat treating. The products are characterized with small thickness, good flatness, outsanding wear resistance, excellent toughness, good weldability, good machinablility, consistent property and quality.

BW450 steel size

Grade

Thickness mm

Width mm

Length mm

BW450

3-12

850-1800

2000-12000

BW450 steel Chemical Composition wt%

Grade

C≤

Si≤

Mn≤

P≤

S≤

Alt≤

Cr≤

Ni≤

Ti

B≤

CEV

BW450

0.35

0.70

1.60

0.020

0.010

0.015

1.10

0.80

0.05

0.005

0.52

CEV = C + Mn/6 + Cr/5 + Mo/5 + B/5 + Cu/15 + Ni/15

BW450 steel plate Mechanical Properties

Grade

Thickness(mm)

Tensile test

Brinell hardness

Impact energy

90° bending

Yield strength ReH,MPa

Tensile strength Rm,MPa

Elongation A50 %

HBW

Impact energy
-40℃
KV2,J

Bending diameter

BW450

3-12

≥1100

≥1300

≥7

450±30

≥20

d = 7a

Note : Transversal specimen is adopted in the tensile test, thus the long axis of specimen is vertical to rolling direction.
ongitudinal specimen is used in impact test, and the impact value is obtained from standard specimen (10 × 10 × 50mm); The impact value shall be reduced with equal proportion if the smaller sized specimen is used, such as 5mm,7.5mm.
Transversal specimen is used in the bending test. d=bending diameter,a=plate thickness

BW450 steel sheet/plate Typical Properties

Parameter

Unit

BW450

CEV(IIW)

%

0.52

Welding crack sensitivity index Pcm

%

0.29

Yield Strength Re

MPa

1200

tensile strength Rm

MPa

14300

Elongation A5 0

%

12

Impact energy  (-40℃)
KV2

J

60

HBW

HBW

450

90° bending

 

D=6t

Young’s modulus(20℃)

GPa

210

Shear modulus(20℃)

GPa

80.8

Poisson ratio(20℃~40℃)

---

0.29

Density

g/cm3

7.85

Thermal conductivity (25℃)

W/(m.K)

48.54

Thermal expansivity(25℃)

1/K

1.254×10-5

Specific heat (25℃)

j/(kg.K)

451.89

Result of block-on-ring wear test

Grade

Average scar width,
mm

Volume loss
mm3

Volume loss rate
mm3 N-1 m-1

Q345B

6.90

10.0577

9.1574E-05

BW450

2.29

0.3638

3.3122E-06

BW450 steel application :
BW450 steels are developed for applications where high wear resistant performance is required, such as dumper, garbage vehicle, concrete mixer truck, industrial air fan, hopper, crusher, machinery for coal, grain , cement, grabbucket, etc.

Shanghai Royal Industry Will return you with high-quality products and complete after-sale service with the lowest price. we committed to exceed customer's expectation on the basis of quality, price, and delivery. We sincerely hope to establish long-term cooperation relationship with you on the basis of mutual benefit, reciprocity and common development. As BW450 Mechanical and BW450 suppliers, we can supply BW450 Chemical, BW450 Mechanical and BW450 standard for you ,please contact us :info@sg295steel.com

If necessary, please leave your message, we will contact you as soon as possible, thank you!

Name:
Email:
Tel:
Message: